{"title":"Leeb Impact Probes","description":"Optional Impact Devices\r\n\r\n\r\n\r\n\r\n\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tImpact device\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tD\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tDC\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tDL\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tD+15\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tC\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tG\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tApplication\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tFor the majority of your hardness testing requirements.\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tUse in very confined spaces, e.g. in holes, cylinders or for internal measure‐ ments on assembled machines.\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tFor measurements in extremely confined spaces or at the base of grooves.\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tFor measurements in grooves or recessed surface.\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tSurface hardened components, coatings, thin walled or impact sensitive components (small measuring indentation).\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tSolid components. E.g. heavy castings and forgings.\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tImpact energy\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t11Nmm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t11Nmm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t11Nmm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t11Nmm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3Nmm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t90Nmm\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tMass of impact body\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5.5g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5.5g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t7.3g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t7.8g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20g\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tTip\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tDiameter\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t2.78mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5mm\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tHardness\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1600HV\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tMaterial\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tTungsten carbide\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tImpact device\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tLength\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t147mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t86mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t202mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t162mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t141mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t254mm\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tDiameter\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t20mm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t30mm\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tWeight\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t75g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t50g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t100g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t80g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t75g\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t250g\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tMax. hardness of sample\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t940HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t940HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t950HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t940HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1000HV\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t650HB\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tThe average roughness of sample\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 1.6μm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 1.6μm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 1.6μm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 1.6μm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 0.4μm\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tRa: 6.3μm\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tMin. weight of sample\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tof compact shape\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5 kg \/ 11lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5 kg \/ 11lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5 kg \/ 11lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5 kg \/ 11lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1.5 kg \/ 3.3 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t15 kg \/ 33 lbs\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\ton solid support\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t2 kg \/ 4.5 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t2 kg \/ 4.5 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t2 kg \/ 4.5 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t2 kg \/ 4.5 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.5 kg \/ 1.1 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t5 kg \/ 11 lbs\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tcoupled on plate\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.05 kg \/ 0.2 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.05 kg \/ 0.2 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.05 kg \/ 0.2 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.05 kg \/ 0.2 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.02 kg \/ 0.045 lbs\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.5 kg \/ 1.1 lbs\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tMin. thickness of sample\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tuncoupled\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t25 mm \/ 0.98 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t25 mm \/ 0.98 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t25 mm \/ 0.98 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t25 mm \/ 0.98 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t15 mm \/ 0.59 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t70 mm \/ 2.73 inch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tcoupled\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3 mm \/ 0.12 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3 mm \/ 0.12 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3 mm \/ 0.12 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t3 mm \/ 0.12 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1 mm \/ 0.04 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t10 mm \/ 0.4 inch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tsurface layer thickness\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.8 mm \/ 0.03 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.8 mm \/ 0.03 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.8 mm \/ 0.03 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.8 mm \/ 0.03 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.2 mm \/ 0.008 inch\r\n\t\t\t\r\n\t\t\t \r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tIndentation size on test surface with 300 HV, 30 HRC\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tdiameter\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.54 mm \/ 0.21 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.54 mm \/ 0.21 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.54 mm \/ 0.21 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.54 mm \/ 0.21 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.38 mm \/0.015 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t1.03 mm \/ 0.04 inch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tdepth\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t24 μm \/ 960 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t24 μm \/ 960 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t24 μm \/ 960 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t24 μm \/ 960 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t12 μm \/ 480 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t53 μm \/ 2120 μinch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tIndentation size on test surface with 600 HV, 55 HRC\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tdiameter\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.45 mm \/0.017 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.45 mm \/0.017 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.45 mm \/0.017 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.45 mm \/0.017 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.32 mm \/ 0.012 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.9 mm \/ 0.035 inch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tdepth\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t17 μm \/ 680 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t17 μm \/ 680 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t17 μm \/ 680 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t17 μm \/ 680 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t8 μm \/ 2560 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t41 μm \/ 1640 μinch\r\n\t\t\t\r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tIndentation size on test surface with 800 HV, 63 HRC\r\n\t\t\t\r\n\t\t\t\r\n\t\t\tdiameter\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.35 mm \/ 0.013 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.35 mm \/ 0.013 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.35 mm \/ 0.013 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.35 mm \/ 0.013 inch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t0.30 mm \/ 0.011 inch\r\n\t\t\t\r\n\t\t\t \r\n\t\t\r\n\t\t\r\n\t\t\t\r\n\t\t\tdepth\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t10 μm \/ 400 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t10 μm \/ 400 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t10 μm \/ 400 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t10 μm \/ 400 μinch\r\n\t\t\t\r\n\t\t\t\r\n\t\t\t7 μm \/ 280 μinch\r\n\t\t\t\r\n\t\t\t \r\n\t\t\r\n\t\r\n\r\n","products":[],"url":"https:\/\/leebhardnesstesters.com\/collections\/leeb-impact-probes.oembed","provider":"CIMETRIX Ltd","version":"1.0","type":"link"}